Raman Scattering Used To Study Breakdown of Optical Fibers
News

Raman Scattering Used To Study Breakdown of Optical Fibers

Raman Scattering Used To Study Breakdown of Optical Fibers
News

Raman Scattering Used To Study Breakdown of Optical Fibers

Credit: Pixabay.
Read time:
 

Want a FREE PDF version of This News Story?

Complete the form below and we will email you a PDF version of "Raman Scattering Used To Study Breakdown of Optical Fibers"

First Name*
Last Name*
Email Address*
Country*
Company Type*
Job Function*
Would you like to receive further email communication from Technology Networks?

Technology Networks Ltd. needs the contact information you provide to us to contact you about our products and services. You may unsubscribe from these communications at any time. For information on how to unsubscribe, as well as our privacy practices and commitment to protecting your privacy, check out our Privacy Policy

Kazan Federal University and OFS found a mechanism of degradation of carbon coating under extreme conditions. The publications was part of a project titled ‘Synthesis and study of a new class of nanocomposite ceramics with a degenerate dielectric constant for optoplasmonic applications’ (supported by Russian Science Foundation); the project lead is Professor Sergey Kharintsev.

As he says, quartz multimode optical fibers are widely used in telecommunications for data transmission, as distributed sensors – for measuring temperature, pressure, mechanical stresses, as well as distributed spectroscopic and acoustic probes in chemically aggressive media at high pressures and temperatures, for example, in oil exploration.


“At high ambient temperatures and pressures, molecular hydrogen H2 and hydroxyl groups OH– can easily penetrate to the core of an optical fiber and enter into chemical reactions. This inevitably leads to an increase in optical loss and, consequently, to a deterioration in the transparency of the fiber. To solve this problem, amorphous carbon is usually used, which effectively protects the optical fiber from moisture and hydrogen. The thickness of the carbon layer is several tens of nanometers, and microstrains of the fiber do not cause a significant deterioration in optical transparency,” comments co-author, PhD student Svetlana Saparina.


While investigating amorphous carbon coatings, the scientists found an irreversible increase in electrical resistance (up to 20%) during repeated heating and cooling cycles in air.


“The increase in resistance is due to the interaction of amorphous carbon with water molecules from the environment. Dissociation of water molecules into H+ and OH- ions and their interaction with edge defects of amorphous carbon lead to the formation of C-H and COOH / C-OH functional groups. Using Raman scattering, we discovered the formation of a C = O carbonyl group when heated above 80 degrees, which annihilates when cooled to room temperature. Thus, the decomposition of water into H + and OH- and their irreversible binding to edge defects lead to the enrichment of the carbon layer with various functional groups. This mechanism leads to an increase in the electrical resistance of amorphous carbon. Defect-enriched carbon provides enhanced diffusion of hydrogen and moisture to the fiber core, making it less transparent,” continues Professor Kharintsev.

Reference
Saparina SV, Fishman AI, Stolov AA, Li J, Kharintsev SS. Water enrichment/depletion of amorphous carbon coatings probed by temperature-dependent dc electrical conductivity and Raman scattering. Applied Surface Science. 2021;570:151052. doi:10.1016/j.apsusc.2021.151052