3D-Printing Advance Mitigates Defects Simultaneously for Failure-Free Metal Parts
Engineers have found a way to simultaneously mitigate three types of defects in parts produced by additive manufacturing.
Complete the form below to unlock access to ALL audio articles.
University of Wisconsin-Madison engineers have found a way to simultaneously mitigate three types of defects in parts produced using a prominent additive manufacturing technique called laser powder bed fusion.
Led by Lianyi Chen, an associate professor of mechanical engineering at UW-Madison, the team discovered the mechanisms and identified the processing conditions that can lead to this significant reduction in defects. The researchers detailed their findings in a paper published on November 16, 2024 in the International Journal of Machine Tools and Manufacture.
“Previous research has normally focused on reducing one type of defect, but that would require the usage of other techniques to mitigate the remaining types of defects,” Chen says. “Based on the mechanisms we discovered, we developed an approach that can mitigate all the defects—pores, rough surfaces and large spatters—at once. In addition, our approach allows us to produce a part much faster without any quality compromises.”
Multiple industries, including aerospace, medical and energy, are increasingly interested in using additive manufacturing (also known as 3D printing) to produce metal parts with complex shapes that are difficult or impossible to create using conventional methods.
But the big challenge is that metal parts created with additive manufacturing have defects—like pores, or “voids,” rough surfaces and large spatters—that significantly compromise the finished part’s reliability and durability. These quality problems prevent 3D-printed parts from being used for critical applications where failure is not an option.
Want more breaking news?
Subscribe to Technology Networks’ daily newsletter, delivering breaking science news straight to your inbox every day.
Subscribe for FREELaser powder bed fusion uses a high-energy laser beam to melt and fuse thin layers of metal powder, constructing a part layer by layer from the bottom up. In this research, the UW-Madison team used an innovative ring-shaped laser beam, provided by a leading laser company called nLight, instead of the usual Gaussian-shaped beam.
The ring-shaped laser beam played a key role in this breakthrough—as did critical “in-situ” experiments, says Jiandong Yuan, the lead author of the paper and a PhD student in Chen’s group.
To see how the material behaved within the part as it was printing, researchers went to the Advanced Photon Source, an ultra-bright, high-energy synchrotron X-ray user facility at Argonne National Laboratory. Combining high-speed synchrotron X-ray imaging, theoretical analysis and numerical simulation, the researchers revealed the defect mitigation mechanisms, which involve phenomena that reduce instabilities in the laser powder bed fusion process.
The researchers also demonstrated that they could use the ring-shaped beam to drill deeper into the material without causing instabilities in the process. This enabled them to print thicker layers, increasing the manufacturing productivity. “Because we understood the underlying mechanisms, we could more quickly identify the right processing conditions to produce high-quality parts using the ring-shaped beam,” says Chen.
Reference: Yuan J, Guo Q, Clark SJ, et al. Revealing mechanisms of processing defect mitigation in laser powder bed fusion via shaped beams using high-speed X-ray imaging. Int J Mach Tools Manufacture. 2024:104232. doi: 10.1016/j.ijmachtools.2024.104232