Upcycling System Developed for Commercial Polyesters
Complete the form below to unlock access to ALL audio articles.
While plastics or synthetic polymers have many useful properties, their mismanagement has resulted in widespread pollution that chokes up our ecosystems. As a solution to this, many synthetic polymers are sent for reprocessing and recycling; polyethylene terephthalate (PET) is one of the most common products frequently seen in the recycling loop in many countries. However, recycling has its own set of problems. During plastic recycling, partial fractions of the polymer chains are decomposed resulting in structurally weak, downgraded polymers. These sub-standard recycled plastics have much reduced properties and are only good for use as solid fuels. This leaves manufacturers with little choice other than to make new plastic products with fast-depleting petroleum feedstocks.
As such, researchers across the world are engaged in developing sustainable cross-linked polymer materials that can be recycled efficiently and cost-effectively. Adding to the growing body of knowledge, Dr. Mikihiro Hayashi, Assistant Professor at Nagoya Institute of Technology, Japan, and his colleague Mr. Takahiro Kimura have developed a simple method to recycle polyester, a common plastic material, into a cross-linked polymer that retains its strength and properties when recycled. Their method centers around transforming polyesters into vitrimersーa new class of polymers possessing dynamic covalent bonds that can reversibly break and reform to create new cross-links. The dynamic covalent bonds render the vitrimer with desirable properties, such as recyclability, reprocessability, and healing capabilities, which are characteristics of high-value functional materials. The study was published on August 1, 2022 in the Journal of Materials Chemistry A.
Talking about their study, Dr. Hayashi says, "Our research demonstrates a one-shot upcycling process of commercial polyesters into cross-linked vitrimers with enhanced thermo-mechanical properties and sustainable functions." He and his colleague created the vitrimers by simply mixing polyester with a cross-linker moleculeー tetra-epoxy, along with the chemical compound 1,8-diazabicyclo[5.4.0]undec-7-ene (DBU) as a catalyst in the presence of tetrahydrofuran as the solvent. The solvent was later evaporated, and the remaining mixture was heated at 200°C for 24 hours, producing a film of vitrimer.
With this method, the cross-linking for producing vitrimer occurs in three quick sequential stagesーhydrolysis (breaking of the polyester bonds), epoxy-opening reaction, and intermolecular transesterification. Discussing the superior mechano-elastic properties of the produced vitrimers, Dr. Hayashi says, "The highly cross-linked and recyclable vitrimer exhibits a 60-fold increase in tensile modulus or Young's modulus and a 10-fold increase in the maximum endurable stress when compared with the original polyester. It also has a gel fraction of nearly 100%." Moreover, the vitrimer was observed to retain its properties even after being ground into fractured pieces and pressed into a flat sheet, which reaffirms its recyclability.
Plastics are essential materials with many benefits and useful properties because they are lightweight, cheap, non-toxic, and easy to produce. However, at the same time, it is necessary to acknowledge and limit the environmental damage they cause. Improving the recyclability of plastic polymers will encourage recycling programs and reduce the use of petroleum, a non-renewable resource. As Dr. Hayashi rightly observes, "The world needs versatile options for recycling synthetic polymers. The method we propose will not only eliminate the use of petroleum-derived chemicals, but it could also be the first step towards a practical and sustainable upcycling system for the future, which adheres to the principles of circular economy and helps realize the SDGs."
As a step forward, the researchers are now planning to devise a more direct transformation of polyesters into vitrimer without using any solvents and are also looking into using their method to transform commercial PET into other highly recyclable materials. If successful, the developed method could lead to a closed loop of plastic production and avert any further environmental crises caused by excessive plastic production.
Reference: Kimura T, Hayashi M. One-shot transformation of ordinary polyesters into vitrimers: decomposition-triggered cross-linking and assistance of dynamic covalent bonds. J Mater Chem A. 2022;10(34):17406-17414. doi: 10.1039/D2TA04110C
This article has been republished from the following materials. Note: material may have been edited for length and content. For further information, please contact the cited source.