Vibrant Blue Pottery Pigments, Now With Less Cobalt

Tiles produced bright colors when glazed with a new blue pigment.
Credit: Adapted from ACS Applied Optical Materials 2024, DOI: 10.1021/acsaom.3c00419.
Listen with
Speechify
0:00
Register for free to listen to this article
Thank you. Listen to this article using the player above.

Want to listen to this article for FREE?

Complete the form below to unlock access to ALL audio articles.

Read time: 1 minute

Whether ultramarine, cerulean, Egyptian or cobalt, blue pigments have colored artworks for centuries. Now, seemingly out of the blue, scientists have discovered a new blue pigment that uses less cobalt but still maintains a brilliant shine. Though something like this might only happen once in a blue moon, the cobalt-doped barium aluminosilicate colorant described in ACS Applied Optical Materials withstands the high temperatures found in a kiln and provides a bright color to glazed tiles.

Want more breaking news?

Subscribe to Technology Networks’ daily newsletter, delivering breaking science news straight to your inbox every day.

Subscribe for FREE

Many of the brilliant blue pigments — like those in antique Chinese porcelain or works by Claude Monet — make use of cobalt-based compounds, including the famous “cobalt blue.” Though the metal itself is toxic, in mineral form it has high chemical and thermal stability, and those properties make cobalt aluminate one of the only pigments suitable for high-temperature applications, including pottery glazes. Today, cobalt is used in lithium-ion batteries, and demand for the metal ore will likely increase as the need for battery power grows. As a result, scientists including Peng Jiang and colleagues are searching for alternative pigments that require fewer cobalt ions and still maintain a bright blue hue.


The team based their new pigment off a barium feldspar mineral (BaAl2Si2O) that also features high temperature and chemical stability. Compounds containing barium, aluminum, silicon and cobalt were ground together, pressed into a sheet, then heated to above 2550 degrees Fahrenheit to form the pigment. Then the researchers mixed the powder into a ceramic glaze, sprayed it onto tiles and fired them to produce glazed pieces of pottery. The pigment was stable at temperatures up to 3200 degrees — well above the typical firing temperature of a pottery kiln — and only experienced slight color changes when exposed to either acidic or alkaline solutions, demonstrating the compound’s stability. Tiles sprayed with the pigmented glaze maintained a smooth, bright surface that deepened in color as the concentration of cobalt in the pigment increased. The researchers say that this new powder substantially reduces the amount of cobalt needed, resulting in a cheaper, easier-to-produce blue ceramic pigment.


Reference: Wang Z, Wang Q, Liu Q, et al. Application and Properties of Co 2+ -Doped BaAl 2 Si 2 O 8 Blue Pigments in Glazes. ACS Appl Opt Mater. 2024;2(2):313-322. doi: 10.1021/acsaom.3c00419